Print it at higher temp. There's a sweet spot. If you're too hot, it will be brittle. If too cool, the layers will be bonded poorly. Try PETG. Or, maybe even high temp PLA. I have not tried Amopha / nGen, or Nylon, but they may be suitable. My best print was PETG at 255c.